Antimony – Properties – Price – Applications – Production

Antimony-properties-price-application-production

About Antimony

Antimony is a lustrous gray metalloid, it is found in nature mainly as the sulfide mineral stibnite. Antimony compounds have been known since ancient times and were powdered for use as medicine and cosmetics, often known by the Arabic name, kohl.

Summary

Element Antimony
Atomic number 51
Element category Metalloids
Phase at STP Solid
Density 6.697 g/cm3
Ultimate Tensile Strength 11 MPa
Yield Strength N/A
Young’s Modulus of Elasticity 55 GPa
Mohs Scale 3.15
Brinell Hardness 300 MPa
Vickers Hardness N/A
Melting Point 631 °C
Boiling Point 1950 °C
Thermal Conductivity 24 W/mK
Thermal Expansion Coefficient 11 µm/mK
Specific Heat 0.21 J/g K
Heat of Fusion 19.87 kJ/mol
Heat of Vaporization 77.14 kJ/mol
Electrical resistivity [nanoOhm meter] 417
Magnetic Susceptibility −99e-6 cm^3/mol

Applications of Antimony

The largest applications for metallic antimony are an alloy with lead and tin and the lead antimony plates in lead–acid batteries. Alloys of lead and tin with antimony have improved properties for solders, bullets, and plain bearings. Antimony can be used in fire retardants for many commercial and domestic products. Antimony trichloride is used in the manufacturing flame-proofing compounds as well as paints, ceramic enamels, glass and pottery. Other uses include ball bearings and mixing with alloys with percentages ranging from 1 to 20 greatly increasing the hardness and mechanical strength of the lead. The capability to strengthen already strong alloys is its largest and most widespread use.

Antimony-applications

Production and Price of Antimony

Raw materials prices change daily. They are primarily driven by supply, demand and energy prices. In 2019, prices of pure Antimony were at around 45 $/kg.

The British Geological Survey (BGS) reported that in 2005 China was the top producer of antimony with approximately 84% of the world share, followed at a distance by South Africa, Bolivia and Tajikistan.

Antimony-periodic-table

Source: www.luciteria.com

Mechanical Properties of Antimony

Antimony-mechanical-properties-strength-hardness-crystal-structure

Strength of Antimony

In mechanics of materials, the strength of a material is its ability to withstand an applied load without failure or plastic deformation. Strength of materials basically considers the relationship between the external loads applied to a material and the resulting deformation or change in material dimensions. In designing structures and machines, it is important to consider these factors, in order that the material selected will have adequate strength to resist applied loads or forces and retain its original shape. Strength of a material is its ability to withstand this applied load without failure or plastic deformation.

For tensile stress, the capacity of a material or structure to withstand loads tending to elongate is known as ultimate tensile strength (UTS). Yield strength or yield stress is the material property defined as the stress at which a material begins to deform plastically whereas yield point is the point where nonlinear (elastic + plastic) deformation begins.

See also: Strength of Materials

Ultimate Tensile Strength of Antimony

Ultimate tensile strength of Antimony is 11 MPa.

Yield Strength of Antimony

Yield strength of Antimony is N/A.

Modulus of Elasticity of Antimony

The Young’s modulus of elasticity of Antimony is N/A.

Hardness of Antimony

In materials science, hardness is the ability to withstand surface indentation (localized plastic deformation) and scratchingBrinell hardness test is one of indentation hardness tests, that has been developed for hardness testing. In Brinell tests, a hard, spherical indenter is forced under a specific load into the surface of the metal to be tested.

Brinell hardness of Antimony is approximately 300 MPa.

The Vickers hardness test method was developed by Robert L. Smith and George E. Sandland at Vickers Ltd as an alternative to the Brinell method to measure the hardness of materials. The Vickers hardness test method can be also used as a microhardness test method, which is mostly used for small parts, thin sections, or case depth work.

Vickers hardness of Antimony is approximately N/A.

Scratch hardness is the measure of how resistant a sample is to permanent plastic deformation due to friction from a sharp object. The most common scale for this qualitative test is Mohs scale, which is used in mineralogy. The Mohs scale of mineral hardness is based on the ability of one natural sample of mineral to scratch another mineral visibly.

Antimony is has a hardness of approximately 3.15.

See also: Hardness of Materials

Antimony – Crystal Structure

A possible crystal structure of Antimony is rhombohedral structure.

crystal structures - FCC, BCC, HCP

In metals, and in many other solids, the atoms are arranged in regular arrays called crystals. A crystal lattice is a repeating pattern of mathematical points that extends throughout space. The forces of chemical bonding causes this repetition. It is this repeated pattern which control properties like strength, ductility, density, conductivity (property of conducting or transmitting heat, electricity, etc.), and shape. There are 14 general types of such patterns known as Bravais lattices.

See also: Crystal Structure of Materials

Crystal Structure of Antimony
Crystal Structure of Antimony is: rhombohedral

Strength of Elements

Elasticity of Elements

Hardness of Elements

 

Thermal Properties of Antimony

Antimony-melting-point-conductivity-thermal-properties

Antimony – Melting Point and Boiling Point

Melting point of Antimony is 631°C.

Boiling point of Antimony is 1950°C.

Note that, these points are associated with the standard atmospheric pressure.

Antimony – Thermal Conductivity

Thermal conductivity of Antimony is 24 W/(m·K).

The heat transfer characteristics of a solid material are measured by a property called the thermal conductivity, k (or λ), measured in W/m.K. It is a measure of a substance’s ability to transfer heat through a material by conduction. Note that Fourier’s law applies for all matter, regardless of its state (solid, liquid, or gas), therefore, it is also defined for liquids and gases.

Coefficient of Thermal Expansion of Antimony

Linear thermal expansion coefficient of Antimony is 11 µm/(m·K)

Thermal expansion is generally the tendency of matter to change its dimensions in response to a change in temperature. It is usually expressed as a fractional change in length or volume per unit temperature change.

Antimony – Specific Heat, Latent Heat of Fusion, Latent Heat of Vaporization

Specific heat of Antimony is 0.21 J/g K.

Heat capacity is an extensive property of matter, meaning it is proportional to the size of the system. Heat capacity C has the unit of energy per degree or energy per kelvin. When expressing the same phenomenon as an intensive property, the heat capacity is divided by the amount of substance, mass, or volume, thus the quantity is independent of the size or extent of the sample.

Latent Heat of Fusion of Antimony is 19.87 kJ/mol.

Latent Heat of Vaporization of Antimony is 77.14 kJ/mol.

Latent heat is the amount of heat added to or removed from a substance to produce a change in phase. This energy breaks down the intermolecular attractive forces, and also must provide the energy necessary to expand the gas (the pΔV work). When latent heat is added, no temperature change occurs. The enthalpy of vaporization is a function of the pressure at which that transformation takes place.

Melting Point of Elements

Periodic Table of Elements - melting point

Thermal Conductivity of Elements

Periodic Table of Elements - thermal conductivity

Thermal Expansion of Elements

Periodic Table of Elements - thermal expansion

Heat Capacity of Elements

Periodic Table of Elements - heat capacity

Heat of Fusion of Elements

Periodic Table of Elements - latent heat fusion

Heat of Vaporization of Elements

Periodic Table of Elements - latent heat vaporization

Antimony – Electrical Resistivity – Magnetic Susceptibility

Antimony-electrical-resistivity-magnetic-susceptibility

Electrical property refers to the response of a material to an applied electric field. One of the principal characteristics of materials is their ability (or lack of ability) to conduct electrical current. Indeed, materials are classified by this property, that is, they are divided into conductors, semiconductors, and nonconductors.

See also: Electrical Properties

Magnetic property refers to the response of a material to an applied magnetic field. The macroscopic magnetic properties of a material are a consequence of interactions between an external magnetic field and the magnetic dipole moments of the constituent atoms. Different materials react to the application of magnetic field differently.

See also: Magnetic Properties

Electrical Resistivity of Antimony

Electrical resistivity of Antimony is 417 nΩ⋅m.

Electrical conductivity and its converse, electrical resistivity, is a fundamental property of a material that quantifies how Antimony conducts the flow of electric current. Electrical conductivity or specific conductance is the reciprocal of electrical resistivity.

Magnetic Susceptibility of Antimony

Magnetic susceptibility of Antimony is −99e-6 cm^3/mol.

In electromagnetism, magnetic susceptibility is the measure of the magnetization of a substance. Magnetic susceptibility is a dimensionless proportionality factor that indicates the degree of magnetization of Antimony in response to an applied magnetic field.

Electrical Resistivity of Elements

Periodic Table of Elements - electrical resistivity

Magnetic Susceptibility of Elements

Application and prices of other elements

Antimony - Comparison of Properties and Prices

Periodic Table in 8K resolution

Other properties of Antimony